Flow Behaviour And Viscoelasticity Of Polypropylene-Kaolin Composites
Melt flow and viscoelastic behaviour of polypropylene kaolin (PP-kaolin) composites were investigated using a single screw extruder at various filler loading, temperature, extrusion cycle and die diameter. It was discovered that for the effect of filler loading, 5 wt% of kaolin loading has caused MF...
| मुख्य लेखक: | |
|---|---|
| स्वरूप: | थीसिस |
| भाषा: | अंग्रेज़ी |
| प्रकाशित: |
2010
|
| विषय: | |
| ऑनलाइन पहुंच: | http://eprints.usm.my/42226/ |
| सारांश: | Melt flow and viscoelastic behaviour of polypropylene kaolin (PP-kaolin) composites were investigated using a single screw extruder at various filler loading, temperature, extrusion cycle and die diameter. It was discovered that for the effect of filler loading, 5 wt% of kaolin loading has caused MFI value and apparent viscosity of the composites to be slightly reduced with respect to pure PP. Whereas, above 5 wt% of kaolin loading the apparent viscosity started to increase. Experimental results also showed that swelling ratio and MFI decreased gradually with increasing amount of filler loading but unexpectedly at 30wt% of kaolin loading, the swelling ratio started to increase proportionately with shear rate. |
|---|